01 Excellent high & low temperature resistance property , range from -200℃ to 1300℃；
02 Good acid and alkali property, the strength of product will retain more than 90% after acid and alkali treatment;
03 Advanced electrical insulation property and ageing resistance property;
04 Advanced heat-insulating property;
05 Low smoke, non-toxic, good flame retardant, meeting the standard of the ROHS.

Size	FP0.6	FP0.8	FP1.0	FP1.5	FP2.0	FP2.5	FP3.0	FP4.0	FP5.0
Thickness（mm）	0.60	0.80	1.00	1.50	2.00	2.50	3.00	4.00	5.00
Range of thickness（mm）	0.50~0.70	0.70~0.90	0.90~1.10	1.35~1.65	1.80~2.20	2.25~2.75	2.70~3.30	3.60~4.40	4.50~5.50
Areal density（g/m2）	60	80	100	200	250	300	400	550	700
Range of areal density（g/m2）	50~70	70~90	90~110	180~220	225~275	270~330	360-440	495-605	630~770

Typical technical data sheet

Test item	Standard	Technic index
Appearance	——	Smooth , no impurities
1000V DC  Insulating property	Under condition of 1000V DC, test time 60s	Insulation resistance≥500MΩ
Fibre ID	——	5.5~7.5μm
Tensile strength	GBT 17911-2018	≥200kPa
Flame retardance property	UL94-V0	Meet with
Thermal conductivity	GB/T 10297-2015	≤0.04w/m·k
ELV	EU ELV Directive 2000/53/EC	Meet limit requirements

Testing data sheet

①  Tiered temperature test for heat-insulating property

Type	200℃	400℃	600℃	600℃ insulation rate/%
FP0.8	69.5 ℃	202.7 ℃	373.4 ℃	37.8
FP1.0	65.2 ℃	195.7℃	347.3 ℃	42.1
FP1.5	58.8 ℃	182.0 ℃	318.0 ℃	47.0
FP3.0	45.9℃	120.2 ℃	235.1℃	60.8
FP4.0	42.6℃	108.7 ℃	217.1 ℃	63.8
FP5.0	34.0 ℃	86.2 ℃	174.3 ℃	70.9

②  Level pressure (under 0.9MPa) test for heat-insulating property

Type	Hot side T/℃	10min cold noodles T/℃	30min cold noodles T/℃	30min insulation rate/%
FP0.8	400	297.7	322.6	19.4
FP1.0	400	280.5	311.1	22.2
FP1.5	400	269.4	300.8	24.8
FP3.0	400	241.1	279.7	30.1
FP4.0	400	216.4	260.2	34.9
FP5.0	400	192.1	238.7	40.3

With very lower powder drop rate and the characters of easily cutting and production, it can be used directly as a independent product, or can be used for electrical equipment, electronic products, and battery cells based on its advanced series of properties after be canned. 

    

The product is easy to cut and process, with extremely low powder loss rate. It can be used directly, and can also be used in the fields of heat insulation and fire prevention of battery cells after packaging, insulation and flame retardancy of electronic products, aerogel thermal insulation composite materials, sealing of high-temperature appliances, heat insulation of furnace wall lining, resin based heat insulation and fire prevention composite materials, etc.